作者
Yanxin Sui,Huili Liang,Wenxing Huo,Xiaozhi Zhan,Tao Zhu,Zengxia Mei
标识
DOI:10.1088/2752-5724/ad19e1
摘要
Abstract Amorphous Ga 2 O 3 (a-Ga 2 O 3 ) has been attracting more and more attention due to its unique merits such as wide bandgap (∼4.9 eV), low growth temperature, large-scale uniformity, low cost and energy efficient, making it a powerful competitor in flexible deep ultraviolet (UV) photodetection. Although the responsivity of the ever-reported a-Ga 2 O 3 UV photodetectors (PDs) is usually in the level of hundreds of A/W, it is often accompanied by a large dark current due to the presence of abundant oxygen vacancy ( V O ) defects, which severely limits the possibility to detect weak signals and achieve versatile applications. In this work, the V O defects in a-Ga 2 O 3 thin films are successfully passivated by in-situ hydrogen doping during the magnetron sputtering process. As a result, the dark current of a-Ga 2 O 3 UV PD is remarkably suppressed to 5.17 × 10 −11 A at a bias of 5 V. Importantly, the photocurrent of the corresponding device is still as high as 1.37 × 10 −3 A, leading to a high photo-to-dark current ratio of 2.65 × 10 7 and the capability to detect the UV light with the intensity below 10 nW cm −2 . Moreover, the H-doped a-Ga 2 O 3 thin films have also been deposited on polyethylene naphtholate substrates to construct flexible UV PDs, which exhibit no great degradation in bending states and fatigue tests. These results demonstrate that hydrogen doping can effectively improve the performance of a-Ga 2 O 3 UV PDs, further promoting its practical application in various areas.
科研通智能强力驱动
Strongly Powered by AbleSci AI