Combustion-synthesised TiAl/NiAl layered intermetallic composite: synthesis, phase composition, and microstructure

The joining of different intermetallics (e.g. NiAl, TiAl) is important for high-temperature applications. In this study, self-propagating high-temperature synthesis was used for simultaneous joining of (Ni+Al) and (Ti+Al) layered samples of the stoichiometric compositions. The main advantage of such joining by self-propagating high-temperature synthesis is that it could be done at ambient temperature without the use of a furnace. The applied load during combustion synthesis was used to improve the contact between the Ni-Al and Ti-Al layers. The obtained results demonstrate that TiAl/NiAl intermetallics were successfully joined together with a bonding interface of about 170 μm thickness. XRD analysis has shown that the joining area consists of NiAl, TiAl, Ti3Al, and NiTiAl2 phases. The SEM data analysis of the transition zone of NiAl-TiAl conjunction has revealed that the transition zone consists of several intermediate layers: a polycrystalline NiAl layer; an intermediate layer based on Ni-Al-Ti containing NiTiAl2 phase; a layer based on Ni-Al-Ti with mixed dendritic and eutectic regions; and a polycrystalline TiAl layer.The measured microhardness of the transition zone varies from 3200 up to 13,600 MPa with the maximum microhardness of 1355 ± 45 MPa corresponding to the layer identified as the NiTiAl2 phase.