Phase Transformation and Deformation Mechanisms in a Cold-Rolled Ti-5at.%Al Alloy

The phase transformations, deformation mechanisms and their correlation in a cold-rolled Ti-5at.%Al alloy were investigated. Two types of phase transformation from a hexagonal close-packed (HCP) structure to a face-centered cubic (FCC) structure were observed: the basal-type (B-type) with an orientation relationship of HCP// FCC and {0001}HCP//{111}FCC, and the prismatic-type (P-type) with an orientation relationship of HCP// FCC and {1010}HCP//{110}FCC. The two types of transformation can both accommodate the strain along the axis of the HCP matrix. With the proceeding of deformation, different deformation mechanisms were activated in the FCC and the HCP structures, respectively, which led to a faster grain refinement rate in the FCC structure than in the HCP matrix. Deformation twins with zero macroscopic strain were prevalent in the FCC domains produced by the B-type transformation, while deformation twins with macroscopic strain were normally observed in the FCC domains produced by the P-type transformation. This is in accordance with the lattice mismatches produced during phase transformation. The easy occurrence of deformation twinning in the FCC structure contributed significantly to the grain refinement process. In addition, the interaction between neighboring FCC domains produced by the two types of phase transformation also accelerated the grain refinement process.