Mesoporous cellulose-chitosan composite hydrogel fabricated via the co-dissolution-regeneration process as biosorbent of heavy metals

Developing low-cost and high-performance biosorbent for water purification continues drawing more and more attention. In this study, cellulose-chitosan composite hydrogels were fabricated via a co-dissolution and regeneration process using a molten salt hydrate (a 60 wt% aqueous solution of LiBr) as a solvent. The addition of chitosan not only introduced functionality for metal adsorption but also increased the specific surface area and improved the mechanical strength of the composite hydrogel, compared to pure cellulose hydrogel. Batch adsorption experiments indicated that the composite hydrogel with 37% cellulose and 63% chitosan exhibited an adsorption capacity of 94.3 mg/g (1.49 mmol/g) toward Cu2+ at 23 °C, pH 5, and initial metal concentration of 1500 mg/L, which was 10 times greater than the adsorption capacity of pure cellulose hydrogel. Competitive adsorption from a mixed metals solution revealed that the cellulose-chitosan composite hydrogel exhibited selective adsorption of the metals in the order of Cu2+ > Zn2+ > Co2+. This study successfully demonstrated an innovative method to fabricate biosorbents from abundant and renewable natural polymers (cellulose and chitosan) for removing metal ions from water.