Effect of electrochemical cycling on microstructures of nanocomposite silicon electrodes using hyperpolarized 129Xe and 7Li NMR spectroscopy

The microstructural stability of composite electrodes during electrochemical cycling is critically important as it dictates the performance of Li-ion batteries. The issue becomes even more important for the high capacity alloying anode such as silicon that typically exhibits dramatic lithiation–delithiation-induced volume changes. The solid electrolyte interphase (SEI) layer formed on the active electrode surface has a profound effect on the overall microstructural stability of composite electrodes. An ideal SEI layer allows Li+ ions in and out of the electrode, but is an insulator to electrons, preventing the electrolyte from being further reduced. However, the SEI layers formed during initial lithiation may experience changes or degradation with subsequent cycling, adversely affecting the electrode performance. A combination of hyperpolarized 129Xe and 7Li nuclear magnetic resonance spectroscopies was applied to probe the microstructures of nanocomposite silicon electrodes at various stages of the lithiation–delithiation cycle. The results obtained from this study shed light on the degradation mechanism of nanocomposite Si electrodes upon electrochemical cycling and should prove useful in the effort to design more robust electrodes in the future.