Optical properties and band alignments in ZnTe nanoparticles/MoS2layer hetero-interface using SE and KPFM studies

Integration of a layered two-dimensional (2D) material with a non-2D material provides a platform where one can modulate and achieve the properties desired for various next-generation electronic and opto-electronic applications. Here, we investigated ZnTe nanoparticles/MoS2 hetero-interfaces with the thickness of the MoS2 varying from few to multilayer. High-resolution transmission electron microscopy was used to observe the crystalline behaviour of the ZnTe nanoparticles, while the number of MoS2 layers was investigated using Raman measurements. Spectroscopic ellipsometry (SE) analysis based on the five-layer fitting model was used to analyse the optical behaviour of the heterojunction, where the excitonic features corresponding to the MoS2 layers and absorption features due to the ZnTe nanoparticles are observed. From the Kelvin probe force microscopy (KPFM) measurements, the surface potential (SP) of the ZnTe nanoparticles/MoS2 is found to be different in comparison with the SP of the ZnTe nanoparticles and MoS2, which is indicative of the charge transfer at the ZnTe nanoparticles/MoS2 hetero-interface. Various parameters obtained using SE and KPFM measurements were used to propose energy band alignments at the ZnTe nanoparticles/MoS2 hetero-interface. In addition, an interface photovoltage of 193 mV was obtained by carrying out KPFM measurements under illuminating condition.