Thermally stimulated current and charge decay studies in polypropylene

A study of thermally stimulated charge-decay (TSCD) in conjunction with that of short-circuit thermally stimulated current (TSC) is undertaken in unilaterally metallized 26 μm thick polypropylene (PP) films. The films are negatively corona charged with various corona voltages varying from 7 to 9 kV at temperatures of 313 K and above and the charge stability of such samples is investigated using the above two techniques. The TSCDs and TSCs indicate a considerable increase in the stability of charge in the samples charged above 353 K which is considered to be due to the localization of charge carriers in deep traps at higher charging temperatures. The present study thus confirms that stable electrets suitable for practical use can be obtained by corona charging at higher temperatures. Das Abklingen des thermisch stimulierten Stromes (TSCD) wird in Verbindung mit dem thermisch stimulierten Kurzschlußstrom (TSC) in einseitig metallisierten 26 μm dickcn Polypropylenschichten (PP) untersucht. Die Schichten werden negativ koronageladen mit unterschiedlichen Koronuspannungen zwischen 7 und 9 kV bei Temperaturen von 313 K und darüber, wobei mit den genannten Methoden die Ladungsstabilität derartiger Proben untersucht wird. Die Ergebnisse der TSCD und TSC zeigen einen beträchtlichen Anstieg der Ladungsstabilität in den oberhalb 353 K geladenen Proben, und es wird angenommen, daß er durch die Lokalisierung von Ladungsträgern in tiefen Haftstellen bei höheren Temperaturen verursacht wird. Die Untersuchung bestätigt somit, daß stabile Elektrete, die für den praktischen Gebrauch geeignet sind, durch Koronaauf ladung bei höheren Temperaturen erhalten werden können.