Effect of blend ratio on Mooney scorch time of rubber blends

The Mooney scorch times of three rubber blends [epoxidized natural rubber (ENR) 50/SMR L, ENR 50/styrene butadiene rubber (SBR), and Standard Malaysian Rubber SMR L/SBR] were studied in the temperature range of 120–160°C using an automatic Mooney viscometer. N-Cyclohexyl-2-benzothiazyl sulfenamide was used as the accelerator, and the rubber formulation was based on the conventional vulcanization system. Results for the blends investigated indicate that a negative deviation of scorch time from the interpolated value was observed, especially for temperatures lower than 130°C. This observation was attributed to the induction effect of the ENR 50 in the ENR 50/SMR L and ENR 50/SBR blends to produce more activated precursors to crosslinks, thus enhancing interphase crosslinking. To a lesser extent, SMR L also exhibited such an induction effect in the SMR L/SBR blend. At 120°C, maximum induction effect occurred at around a 40% blend ratio of ENR 50 and SMR L in the respective blends. For the filled stock at 140°C, carbon black exhibited less effect on the scorch property of the blends compared to silica. © 1998 John Wiley & Sons, Inc. J Appl Polym Sci 69: 1301–1305, 1998