Abnormal annealing-induced strengthening in Ni39.3Al15.7Fe45 eutectic medium entropy alloy

Cold-working combined with annealing is frequently used to enhance strength of traditional alloy materials. However, this thermal-mechanical processing is not adapted to the preparation for some near net shape parts. In this paper, a dual-phase Ni39.3Al15.7Fe45 eutectic medium entropy alloy (EMEA) was prepared by vacuum arc melting and abnormal annealing-induced strengthening is demonstrated and analyzed via XRD, SEM, EDS, TEM and room temperature tensile testing. It is found that the Ni39.3Al15.7Fe45 EMEA is composed of FCC solid solution phase and BCC phase. After annealing, ordered L12 phase precipitated from FCC solid solution, which induces a significant increment of tensile strength and a weak decrease of tensile plasticity. The tensile strength and elongation are 991 MPa and 24.1 % at as-cast state, the tensile strength and elongation are 1279 MPa and 22.4 % after annealing at 700 °C for 1 h.