Crystallization Control and Defect Passivation via a Cross-Linking Additive for High-Performance FAPbBr3 Perovskite Solar Cells

Bromine-based hybrid perovskites exhibit excellent performance as the top layer of tandem cells, but their overall efficiency as single-junction devices is still very limited. In this work, trimethylolpropane ethoxylated triacrylate (TET), which can form a cross-linking polymer at the grain boundary after heating at 150 °C, is introduced as an additive in FAPbBr 3 -based perovskite solar cells. The FAPbBr 3 film with TET exhibits pinhole-free crystal grains with a large grain size. With a concentration of 5 mg/mL TET, the average grain size increases from 313 to 505 nm. What is more, Raman spectroscopy and X-ray photoelectron spectroscopy demonstrate that the cross-linked TET has a strong interaction with FAPbBr 3, which can passivate the defects of grain boundaries. Therefore, the FAPbBr 3 -based perovskite solar cells with TET achieve a power conversion efficiency of 8.93%. As we know, this is the highest value in FAPbBr 3 -based hybrid perovskites with an inverted planar structure. This work provides a new insight into the in situ cross-linking additive TET, which only exists at the grain boundary, does not enter the lattice, and has a crystallization control and defect passivation effect on FAPbBr 3 thin films, which will provide a new direction for further improving the performance of FAPbBr 3 perovskite solar cells.