An XPS investigation of the oxidation/corrosion of melt-spun Mg

The oxide films formed on the surfaces of melt-spun Mg exposed to air, immersed in distilled water or 3% NaCl solution saturated with Mg(OH)2 have been investigated by X-ray photoelectron spectroscopy (XPS). High resolution XPS spectra revealed two distinct oxygen species on the surface films: one assigned to O2− in MgO, the other to OH− in Mg(OH)2. Depth profiling revealed that the two species had different depth distributions in the films. The oxide film formed in air comprised a contamination outer layer and a relatively thick (5–6 nm) predominantly MgO inner layer. The film formed in distilled water or 3% NaCl solution saturated with Mg(OH)2 was mainly a mixture of Mg(OH)2 and MgO. Mg(OH)2 was predominant at the top layer and decreased gradually with depth while MgO exhibited the opposite behavior. The corrosion product formed in 3% NaCl solution was more hydrated and much thicker that the films formed in the other two conditions. Cl− ion was incorporated in the oxide film formed in 3% NaCl solution. There exists both partial and complete dissociation of adsorbed water when melt-spun pure Mg ribbons are immersed in distilled water or 3% NaCl solution saturated with Mg(OH)2.