Room temperature ferromagnetism in ZnO films due to defects

ZnO films were prepared by pulsed laser deposition on a-plane sapphire substrates under N2 atmosphere. Ferromagnetic loops were obtained with the superconducting quantum interference device at room temperature, which indicate a Curie temperature much above room temperature. No clear ferromagnetism was observed in intentionally Cu-doped ZnO films. This excludes that Cu doping into ZnO plays a key role in tuning the ferromagnetism in ZnO. 8.8% negative magnetoresistance probed at 5K at 60kOe on ferromagnetic ZnO proves the lack of s-d exchange interaction. Anomalous Hall effect (AHE) was observed in ferromagnetic ZnO as well as in nonferromagnetic Cu-doped ZnO films, indicating that AHE does not uniquely prove ferromagnetism. The observed ferromagnetism in ZnO is attributed to intrinsic defects.