Shear Localization and Comminution of Granular and Fragmented Silicon Carbide

Granular and pre-fractured bulk silicon carbide were subjected to high strain, high-strain-rate deformation by radial symmetric collapse of a thick-wall cylinder.Profuse shear-band formation was observed, indicating the deformation had inhomogeneous characteristics.The granular silicon carbide had lower shear-band displacement, spacing between shear bands and thickness of shear bands than the pre-fractured silicon carbide.Bimodal particle size distribution was seen inside the shear bands for both materials.The shear localization in the granular silicon carbide was primarily due to particle break-up (comminution) and rearrangement of the comminuted particles.The shear bands in the pre-fractured silicon carbide were formed through the incorporation of fragments from the shear-band interfaces and the erosion of fragments inside the shear band.R&um& Des Bchantillons de carbure de silice prB-fragment& et granulaires ont Bt B soumis A des hautes dBformations A hautes vitesses par I'implosion symktrique d'un cylindre A parois Bpaisses.La formation de bandes de cisaillement a Bt B obsewBe, indiquant que la deformation est inhomogene.Le cisaillement dans les bandes la distance entre les bandes et I'Bpaisseur des bandes dtaient plus faibles pour le carbure de silice gmulB.Une distribution de taille de poudre bimodale a 6tB observee dans les bandes pour les deux mattriaux.La formation de bandes de cisaillement a kt6 produite principalement par la fragmentation des poudres et la &organisation des particules pulvBrisBes.Les bandes de cisaillement dans le materiau pre-fissure sont fonnees par l'addition de fragments partir des interfaces de la bande de cisaillement et par I'drosion des fragments I'interieur de la bande de cisaillement.