Mechanical and degradation properties of degradable cover materials for sugarcane leaves

Mulch was prepared using composted sugarcane leaves, with polyvinyl alcohol and cationic starch as adhesives, through compression molding. The study aimed to investigate the effects of different adhesives on the mechanical properties, thermal oxidative degradation performance, and biodegradability of the covering materials. The results indicated that, when the adhesive dosage was consistent, cover material A, which utilized polyvinyl alcohol as the adhesive, exhibited higher tensile strength and elongation at break compared to cover material B, which employed a blend of polyvinyl alcohol and cationic starch. Specifically, at an adhesive dosage of 20%, cover material A achieved a tensile strength of 0.46 MPa and an elongation at break of 7.72%, representing the highest values among all experimental groups. There was minimal disparity in the thermal oxidative degradation performance between materials prepared with either adhesive; however, a higher quantity of adhesive led to decreased biodegradability performance. After being buried in soil for 120 days, the degradation exceeded 40% for both materials, resulting in loss of their original shape and strength properties. In conclusion, while sugarcane leaves-based biodegradable materials demonstrate favorable degradation performance, further enhancements are necessary to improve their mechanical properties. These materials have potential applications as substitutes for plastic mulch.