Deformation processes related to interfacial boundaries in two-phase γ-titanium aluminides

The deformation behaviour of two-phase (α2 + γ) titanium aluminide alloys with a lamellar microstructure was investigated by conventional and high resolution electron microscopy. With regard to the mechanical properties, the structures of the interfacial boundaries occurring in these materials are characterized and the interaction mechanisms of the deformation processes with these interfaces is investigated. Accordingly, the misfit dislocations present at semicoherent α2/γ and γ/γ interfaces assist the generation of dislocations and deformation twins. On the other hand, the semicoherent interfaces act as very effective barriers impeding the propagation of slip across the lamellae. Das Verformungsverhalten von zweiphasigen (α2 + γ) Titan-Aluminid Legierungen mit einer lamellaren Mikrostruktur wurde mit konventioneller und hochauflösender Elektronenmikroskopie untersucht. Die Struktur der in diesen Materialien vorhandenen Phasengrenzflächen wurde im Hinblick auf die mechanischen Eigenschaften charakterisiert. Auβerdem wurden die Wechselwirkungsprozesse zwischen den Verformungsmechanismen und diesen Grenzflächen untersucht. Die an den semikohärenten Grenzflachen vorhandenen Anpassungsversetzungen unterstützen danach die Erzeugung von Versetzungen und Verformungszwillingen. Die semikohärenten Grenzflächen sind andererseits sehr starle Hindernisse für die Ausbreitung von Gleitprozessen quer zu den Lamellen.