Crown Ether Electrolyte Induced Li2O2 Amorphization for Low Polarization and Long Lifespan Li‐O2 batteries

Abstract Lithium‐oxygen batteries possess an extremely high theoretical energy density, rendering them a prime candidate for next‐generation secondary batteries. However, they still face multiple problems such as huge charge polarization and poor life, which lay a significant gap between laboratory research and commercial applications. In this work, we adopt 15‐crown‐5 ether (C15) as solvent to regulate the generation of discharge products in lithium‐oxygen batteries. The coronal structure endows C15 with strong affinity to Li + , firmly stabilizes the intermediate LiO 2 and discharge product Li 2 O 2 . Thus, the crystalline Li 2 O 2 is amorphized into easily decomposable amorphous products. The lithium‐oxygen batteries assembled with 0.5 M C15 electrolyte show an increased discharge capacity from 4.0 mAh cm −2 to 5.7 mAh cm −2 and a low charge overpotential of 0.88 V during the whole lifespan at 0.05 mA cm −2 . The batteries with 1 M C15 electrolyte can cycle stably for 140 cycles. Furthermore, the amorphous characteristic of Li 2 O 2 product is preserved when matched with redox mediators such as LiI, with the charge polarization further decreasing to 0.74 V over a cycle life of 190 cycles. This provides new possibilities for electrolyte design to promote Li 2 O 2 amorphization and reduce charge overpotential in lithium‐oxygen batteries.