Porthole die extrusion of aluminum 6063 industrial scrap by shear assisted processing and extrusion

Shear Assisted Processing and Extrusion (ShAPE) is presented as a new manufacturing technology for converting aluminum scrap directly into extruded products. In this work, a porthole die configuration is integrated within the rotating ShAPE process to extrude circular, square, trapezoidal, and two-cell trapezoidal profiles from aluminum alloy 6063 industrial scrap. This is the first time that a rotating billet has been used to impart severe plastic deformation (SPD) during extrusion of noncircular profiles. Microstructural characterization is presented for a trapezoidal profile having an average grain size of 6.7 µm in the as-extruded condition. Dimensional stability was evaluated by measuring wall thickness along the extrusion length; the thickness varied by <5%. Round tubes achieved yield strength (246.9 ± 10.4 MPa), ultimate tensile strength (270.8 ± 9.6 MPa), and uniform elongation (16.5 ± 2.4%) exceeding industry standards.