Hydrothermal preparation and low temperature magnetic properties of Mn(OH)2

Manganese hydroxide,Mn(OH)2, was prepared using hydrothermal techniques. The magnetic properties of the compound were investigated between 4.2 and 273 K. Mn(OH)2 is antiferromagnetic with a Néel temperature of 12 K. Neutron diffraction powder patterns were obtained at 4.2 K and at 300 K. The magnetic superlattice reflections were indexed on the basis of a hexagonal unit cell with the dimensions aM = a(3), and cM = 2c where a = 3.322 Å and c = 4.734 Å are the dimensions of the chemical unit cell. An antiferromagnetic sequence of the spins along the c axis, and a screw spiral propagating in the basal plane describes the magnetic structure. The hydrogen atom position of the crystal structure is determined. L'hydroxyde de manganèse Mn(OH)2 a été préparé par synthèse hydrothermale. Les propriétés magnétiques de ce composé ont étéétudiées entre 4.2 K et 273 K. Mn(OH)2 est antiferromagnétique, la température du point de Néel est 12 K. Les diagrammes de diffraction neutronique sur poudre ont été enregistrés à 4.2 K et 300 K. Les réflexions magnétiques sont indexées sur la base d'une maille hexagonale de dimensions aM = a(3), et cM = 2c où a = 3,322 Å et c = 4,734 Å sont les dimensions de la maille chimique. La structure magnétique est décrite par un arrangement antiferromagnétique de spins selon l'axe c couplé avec une hélice, les spins tournant d'un angle de 2π/3 dans un plan perpendiculaire au plan de base. La position de l'atome d'hydrogène dans la structure cristalline est déterminée.