Synthesis of SiC/BN nanocomposite powders by carbothermal reduction and nitridation of borosilicate glass, and the properties of their sintered composites

A new synthetic method for the fabrication of SiC/BN nanocomposites was devised to attain strong machinable ceramics. SiC/BN nanocomposites that contained 10, 20, and 30 vol% hexagonal BN (h-BN) were successfully fabricated by sintering SiC-BN nanocomposite powders by carbothermal reduction and nitridation of borosilicate glass powders. Homogeneous mixtures of silica (SiO(2)), boric acid (H(3)BO(3)), and carbon powder were heated in a nitrogen atmosphere to synthesize SiC-BN nanocomposite powders. Borosilicate glass was obtained by reacting SiO(2) and B(2)O(3) above 800 °C, and SiC and turbostratic BN (t-BN) were obtained by reacting borosilicate glass with carbon powder and nitrogen gas at 1500 °C. Carbothermal reduction followed by nitridation yielded SiC-BN nanocomposite powder composed of nanosized SiC and t-BN. By hot-pressing nanocomposite SiC-BN powders containing 7 wt% Al(2)O(3) and 2 wt% Y(2)O(3), machinable SiC/BN nanocomposites were obtained without a significant decrease in their fracture strength.