Anisotropy in tensile behavior of an extruded Mg-4.50Zn-1.13Ca (wt.%) alloy

Abstract The present study investigated anisotropy in tensile behavior of an extruded Mg-4.50Zn-1.13Ca (wt.%) alloy through tensile testing along different tilt angles relative to the extrusion direction. Results showed that the as-extruded Mg-4.50Zn-1.13Ca (wt.%) alloy exhibited anisotropy in tensile behavior due to the formation of basal texture. Basal slip, prismatic slip and tensile twinning were the dominant deformation modes depending on the tensile direction. Prismatic slip was the dominant deformation mode for samples with small tilt angle ( θ = 0° and 22.5°). Basal slip was activated when the tilt angle was increased, which also resulted in the decrease of yield strength. Tensile twinning was responsible for the yielding of the samples with high tilt angles ( θ = 67.5° and 90°). The ductility was significantly reduced at high tilt angle, which was mainly attributed to the appearance of tensile twinning during tensile deformation.