Branched core-shell a-TiO2@N-TiO2 nanospheres with gradient-doped N for highly efficient photocatalytic applications

A branched core-shell nanosphere composed of an anatase TiO2 (a-TiO2) core and a TiO2 nanobranch shell with gradient-doped N (a-TiO2@N-TiO2) is synthesized by a simple in situ doping method, in which mixed crystal anatase-rutile TiO2 (ar-TiO2) nanosphere is first prepared by oxidizing Ti using H2O2, and then is etched by NH3·H2O to form (NH4)2TiO3 nanobranches, which is converted into a-TiO2@N-TiO2 following an ambient annealing process. The diameter of a-TiO2 core is ∼500 nm, and the thickness of N-TiO2 branched shell is ∼100 nm with gradually increased N concentration from the bottom to the edge. Ultra-thin amorphous coating layers on the branches are also observed. The morphology of the composites could be further tuned by the amount of NH3·H2O, and its effect on the photocatalytic performance is also investigated. The optimized a-TiO2@N-TiO2 shows an outstanding hydrogen evolution rate of 308.1 µmol g−1 h−1 under air mass (AM) 1.5 illumination, and also exhibits highly active in photocatalytic degradation of various refractory organic pollutants, including organic dyes, phenols, antibiotics, and personal care products, with removal ratios higher than 96% after 2 h operation. This can be due to the gradient-doped N-TiO2 nanobranches, which not only provide bending band structure and defect level derived from the N impurities and O vacancies, resulting the formation of n-n+ heterojunctions to improve the charge separation, but also enhance the charge transfer at the liquid-solid interface due to the numerous nanobranches and amorphous coating layers.