Three-dimensional printing akermanite porous scaffolds for load-bearing bone defect repair: An investigation of osteogenic capability and mechanical evolution

) porous materials manufactured by ceramic ink writing three-dimensional printing technique were investigated systematically in a critical size femur defect model, in comparison with the clinically available β-tricalcium phosphate porous bioceramic. Such three-dimensional printed akermanite scaffolds possess fully interconnected pores of ∼280 × 280 µm in size and over 50% porosity with appreciable compressive strength (∼71 MPa), that is 7-fold higher than that of the β-tricalcium phosphate porous bioceramics (∼10 MPa). After 6 weeks and 12 weeks of implantation, the percentage of newly formed bone and more new bone was observed in the akermanite group as compared with the β-tricalcium phosphate group (p < 0.01). Moreover, significant higher mRNA expressions of osteogenic genes were detected in the akermanite group by PCR analysis (p < 0.01). The in vivo mechanical strength decreased during the process of implantation, but maintained a relative high level (∼14 MPa) which was still higher than that of the host cancellous bone (5-10 MPa) at 12 weeks post-implantation. On the contrary, the β-tricalcium phosphate scaffold always exhibited a very low mechanical strength (∼8 MPa). These results suggest that the three-dimensional printed akermanite scaffolds are promising for the bone tissue regeneration and repair of load-bearing bone defects.