Phase transformation behavior and mechanical properties of HyFlex EDM nickel-titanium endodontic rotary instrument: Evaluation at body temperature

Temperature-dependent phase compositional changes influence the mechanical properties of heat-treated nickel-titanium (NiTi) rotary instruments. This study evaluated the phase composition, bending properties, and cyclic fatigue resistance of HyFlex EDM NiTi rotary instruments against differently heat-treated and non-heat-treated NiTi instruments at body temperature (BT). HyFlex EDM OneFile (EDM) instruments, heat-treated HyFlex CM (CM) and Twisted File (TF) instruments, and non-heat-treated K3 instruments (size #25/.08) were subjected to differential scanning calorimetry, and the martensitic, R-phase, and reverse transformation starting and finishing temperatures were determined. A cantilever bending test and a cyclic fatigue test were conducted at BT (37 °C ± 1.0 °C), and the bending load and number of cycles to failure (NCF) were recorded. Statistical analysis was performed using Kruskal–Wallis and Mann–Whitney U tests (α = 0.05). TF and K3 had reverse transformation finishing temperatures lower than BT, while those for EDM and CM were higher than BT. The bending loads at a 0.5 mm deflection were in the order of EDM < TF < CM < K3 (P < 0.05), and those at a 2.0 mm deflection were EDM < CM and TF < K3 (P < 0.05). EDM had the highest NCF among the four instruments (P < 0.05). The EDM instrument had a reverse transformation finishing temperature higher than BT indicating its martensite/R-phase composition at BT. The EDM instrument had superior flexibility and greater resistance to cyclic fatigue than the CM, TF, and K3 instruments at BT.