Effects of Counterpart Materials on Wear Behavior of Thermally Sprayed STS316 Coatings

This paper deals with the effects of counterpart materials on the wear behavior of thermally sprayed STS316 coatings. STS316 powders were flame-sprayed onto a carbon steel substrate. Dry sliding wear tests were performed using the applied loads of 15 N. AISI52100, $Al_2O_3$, $ZrO_2$ and $Si_3N_4$ balls were used as counterpart materials. Wear behavior of STS316 coatings against different counterpart materials were studied using a scanning electron microscope(SEM) and energy dispersive X-ray spectroscopy (EDS). The results show that the wear behavior of thermally sprayed STS316 coatings strongly depends on the type of counterpart material. Dominant wear mechanism was similar for all studied materials as failure of adhesion film except for Si3N4 used as counterpart material. In the case of Si3N4 used as counterpart material, dominant wear mechanism was abrasion.