Investigation of the Adhesion Layer Formed on Brass Using Field Emission-Scanning Electron Microscope

Abstract Change in the morphological features of the adhesion layer formed on brass was observed with Field Emission-Scanning Electron Microscopy (FE-SEM). The effect of the key compounding ingredients on the morphology of the adhesion layer was studied. Morphology of the various metal sulfides of cobalt, zinc, copper, bronze and brass was also observed with FE-SEM. Fracture mode appeared during the pull-out test was categorized and was correlated with the adhesion strength. The damage on the adhesion layer after humidity aging test was examined by FE-SEM.