Negative differential resistance and resistive switching in SnO2/ZnO interface

We report a very stable negative differential resistance (NDR) and resistive switching (RS) behavior of highly transparent thin films of the SnO2/ZnO bilayer, deposited by magnetron sputtering. When this bilayer of SnO2/ZnO was annealed at temperatures above 400 °C, ZnO diffuses into SnO2 at the threading dislocations and gaps between the grain boundaries, leading to the formation of a ZnO nanostructure surrounded by SnO2. Such a configuration forms a resonant tunneling type structure with SnO2/ZnO/SnO2…….ZnO/SnO2 interface formation. Interestingly, the heterostructure exhibits a Gunn diode-like behavior and shows NDR and RS irrespective of the voltage sweep direction, which is the characteristic of unipolar devices. A threshold voltage of ∼1.68 V and a peak-to-valley ratio of current ∼2.5 are observed for an electrode separation of 2 mm, when the bias is swept from −5 V to +5 V. It was also observed that the threshold voltage can be tuned with changing distance between the electrodes. The device shows a very stable RS with a uniform ratio of about 3.4 between the high resistive state and the low resistive state. Overall, the results demonstrate the application of SnO2/ZnO bilayer thin films in transparent electronics.