Comparison of GRCop-84 to Other High Thermal Conductive Cu Alloys

The mechanical properties of five copper alloys (GRCop-84, AMZIRC, GlidCop Al-15, Cu-1Cr-0.1Zr, Cu-0.9Cr) competing in high temperature, high heat flux applications such as rocket nozzles, were compared. Tensile, creep, thermal expansion, and compression tests are presented. Tests were done on as-received material, and on material which received a simulated brazing heat treatment at 935 C. The 935 C heat treatment weakened AMZIRC, Cu-1Cr-0.1Zr, and Cu-0.9Cr, and the strength of as-received AMZIRC dropped precipitously as test temperatures exceeded 500 C. The properties of GlidCop Al-15 and GRCop-84 were not significantly affected by the 935 C heat treatment. Thus GRCop-84 is better than AMZIRC, Cu-1Cr-0.1Zr, and Cu-0.9Cr at temperatures greater than 500 C. Ductility was lowest in GlidCop Al-15 and Cu-0.9Cr. The creep properties of GRCop-84 were superior to those of brazed AMZIRC, Cu-1Cr-0.1Zr, and Cu-0.9Cr. At equivalent rupture life and stress, GRCop-84 had a 150 C temperature advantage over brazed AMZIRC; for equivalent rupture life and temperature GRCop-84 was two times stronger. The advantages of GRCop-84 over GlidCop Al-15 associated with ease of processing were confirmed by GlidCop s marginal ductility. In the post brazed condition, GRCop-84 was found to be superior to the other alloys due to its greater strength and creep resistance (compared to AMZIRC, Cu-1Cr-0.1Zr, and Cu-0.9Cr) and ductility (compared to GlidCop Al-15)