Designing 1,5‐Naphthyridine‐2,6‐dione‐Based Conjugated Polymers for Higher Crystallinity and Enhanced Light Absorption to Achieve 9.63% Efficiency Polymer Solar Cells

Abstract Highly crystalline conjugated polymers represent a key material for producing high‐performance thick‐active‐layer polymer solar cells (PSCs). However, despite their potential, a limited number of crystalline polymers are used in PSCs because of the lack of highly coplanar acceptor building blocks and insufficient light absorptivity (α < 105) of most donor (D)–acceptor (A)‐type polymers. This study reports a series of novel 3,7‐di(thiophen‐2‐yl)‐1,5‐naphthyridine‐2,6‐dione (NTDT) acceptor‐based conjugated polymers, PNTDT‐2T, PNTDT‐TT, and PNTDT‐2F2T, synthesized with 2,2′‐bithiophene (2T), thieno[3,2‐b]thiophene (TT), and 3,3′‐difluoro‐2,2′‐bithiophene (2F2T) donor units, respectively. PNTDT‐2F2T exhibits superior polymer crystallinity and a much higher absorption coefficient than those of PNTDT‐2T or PNTDT‐TT because of adequate matching between highly coplanar A (NTDT) and D (2F2T) building blocks. A bulk heterojunction solar cell based on PNTDT‐2F2T exhibits a power conversion efficiency of up to 9.63%, with a high short circuit current of 18.80 mA cm−2 and fill factor of 0.70, when a thick active layer (>200 nm) is used, without postfabrication hot processing. The findings demonstrate that the polymer crystallinity and absorption coefficient can be effectively controlled by selecting appropriate D and A building blocks, and that NTDT is a novel and versatile A building block for highly efficient thick‐active‐layer PSCs.