The Preparation of Acryloxyl Group Functionalized Siloxane Polymers and the Study of Their Ultra Violet Curing Properties

Polysiloxane with multiple acryloxyl groups at the terminal site of the polymer chain was synthesized by the condensation reaction between hydroxyl-terminated polysiloxane and acryloyl chloride and used to improve the cross-linking density of UV-curable silicone materials initiated from dual acryloxy-terminated symmetric polysiloxane or single acryloxy-terminated asymmetric polysiloxane with the mixture of Irgacure 1173 and Irgacure 184 at a mass ratio of 1:1 as the photoinitiator. The effects of factors such as initiator composition, UV irradiation time, structure, and molecular weight of linear dual acryloxy-terminated or single acryloxy-terminated asymmetric siloxane oligomers on the gelation yield, thermal properties, water absorption, and water contact angle of UV-cured film were investigated. The synthesized cross-linking density modifier can be copolymerized with acryloxy-functionalized linear polysiloxanes under the action of a photoinitiator to increase the cross-link density of UV-cured products effectively. Both linear dual acryloxy-terminated or single acryloxy-terminated asymmetric siloxane oligomers can be copolymerized with cross-link density modifiers within 20 s of UV irradiation. The gelation yields of the UV-cured products obtained from the dual acryloxy-terminated siloxane oligomers were greater than 85%, and their surface water contact angles increased from 72.8° to 95.9° as the molecular weight of the oligomers increased. The gelation yields of UV-cured products obtained from single acryloxy-terminated asymmetric siloxane oligomers were less than 80%, and their thermal stabilities were inferior to those obtained from the dual acryloxy-terminated siloxane oligomers. However, the water contact angles of UV-cured products obtained from these single acryloxy-terminated asymmetric siloxane oligomers were all greater than 90°.