Progress in Natural Science: Materials International

Boron nitride (BN) was prepared by nitriding pure boron (B) deposited on carbon substrates by chemical vapor deposition (CVD). Thermodynamic analysis of preparing BN by nitriding CVD B at 1200-1550 1C was firstly performed. And then, the effects of nitridation conditions, including temperature, nitridation atmosphere and CVD B microstructure, on the conversion of B to BN were analyzed by scanning electron microscopy (SEM), energy dispersion spectroscopy (EDS), X-ray photoelectron spectroscopy (XPS) and transmission electron microscopy (TEM). Results show that the conversion degree of B to BN firstly increased and then slightly decreased with rising temperature. The nitridation degree was controlled by mutual actions between the nitridation of B and consumption of the effective nitrogen source (NH3). The morphology of products and the reaction mechanism between B and N were influenced by nitridation temperature. At high temperatures (1400-1500 1C), BN with highly ordered microstructure was produced. On using N2-H2 as nitridation atmosphere instead of NH3-H2- N2, no BN was obtained in the studied temperature range. The microstructure and component of BN obtained in nitridation process were little affected by the microstructure of CVD B.