Cu2O-Based Homostructure Fabricated by Electrodeposition Method

The Cu2O-based homostructure thin film was successfully fabricated on FTO glass substrate using conventional electrodeposition method.Prior to the p-Cu2O thin film deposition, cyclic voltammetry (CV) measurement was carried out in order to obtain optimum deposition parameter.Based on the CV result, p-Cu2O thin film was deposited on n-Cu2O with deposition potential of -0.4 V vs Ag/AgCl, solution temperature of 40 • C and pH 12.5, respectively.The deposition time was varied and it was found that the optimum deposition time for Cu2O-based homostructurethin film was 2 h.Structural, morphological, and optical properties were characterized using Xray diffraction, field emission-scanning electron microscope and ultraviolet and visible absorption spectroscopy, respectively.The successful fabrication of homostructure was confirmed using photoelectrochemical measurement.