Sulfate template induced S/O doped carbon nanosheets enabling rich physi/chemi-sorption sites for high-performance zinc ion hybrid capacitors

Zinc ion hybrid capacitors (ZIHCs) are encouraging energy storage devices for large-scale applications. Nevertheless, the electrochemical performance of ZIHCs is often limited by the cathode materials which show low energy density and rate capability practically. One of the efficient strategies to overcome these challenges is the development of advanced carbon cathode materials with abundant physi/chemisorption sites. Herein, we develop a sulfate template strategy to prepare sulfur and oxygen doped carbon nanosheets (SOCNs) as a potential cathode active material for ZIHCs. The as-prepared SOCNs exhibit porous architectures with a large surface area of 1877 m2 g-1, substantial structural defects, and high heteroatom-doped contents (O: 7.9 at%, S: 0.7 at%). These exceptional features are vital to enhancing Zn ion storage. Consequently, the SOCN cathode shows a high capacity of 151 mAh g-1 at 0.1 A g-1, high cycle stability with 83% capacity retention at 5 A g-1 after 4000 cycles, and a superior energy density of 103.1 Wh kg-1. We also investigate the dynamic adsorption/desorption behaviors of Zn ions and anions of the ZIHCs carbon electrodes during the process of charge and discharge by ex-situ experiments. This work highlights the significance of the integration with a large specific surface area and bountiful heteroatoms in carbon electrodes for achieving high-performance ZIHCs.