Wide Bandgap Polymer with Narrow Photon Harvesting in Visible Light Range Enables Efficient Semitransparent Organic Photovoltaics

Abstract Wide bandgap polymer D18 with narrow photon harvesting in visible light range and small molecule N3 with near‐infrared photon harvesting are adopted for building semitransparent organic photovoltaics (OPVs). To find out the optimal D18:N3 weight ratio for semitransparent OPVs, series of opaque OPVs are built with a varied D18:N3 weight ratio. The power conversion efficiency (PCE) and fill factor can be maintained over 16% and 77% in the D18:N3 (0.7:1.6, wt/wt) based opaque OPVs, respectively. The average visible transmittance (AVT) of the corresponding blend films can be achieved over 50%, demonstrating the great potential in fabricating efficient semitransparent OPVs. The semitransparent OPVs based on D18:N3 (0.7:1.6, wt/wt) are fabricated by using 1 nm Au/(10, 15, 20 nm) Ag as cathode. The thickness of Ag layers is varied to balance the optical properties and electrical properties of semitransparent top electrode. The semitransparent OPVs with 10 nm Ag achieve the highest light utilization efficiency of 2.90% with a PCE of 12.91% and an AVT of 22.49%, which should be among the best performance of reported semitransparent OPVs. This work demonstrates that the wide bandgap polymer donor with narrow photon harvesting in visible light range has great potential in preparing efficient semitransparent OPVs.