Preparation and characterization of interpenetration polymer network films based on poly(vinyl alcohol) and poly(acrylic acid) for drug delivery

Abstract A series of full interpenetrating polymer network (full‐IPN) films of poly(acrylic acid) (PAA)/poly (vinyl alcohol) (PVA) were prepared by radical solution polymerization and sequential IPN technology. Attenuated total reflectance‐Fourier transform infrared spectroscopy, swelling properties, mechanical properties, morphology, and glass transition temperature of the films were investigated. FTIR spectra analysis showed that new interaction hydrogen bonds between PVA and PAA were formed. Swelling property of the films in distilled water and different pH buffer solution was studied. Swelling ratio increased with increasing PAA content of IPN films in all media, and swelling ratio decreased with increasing PVA crosslink degree. Tensile strength and elongation at break related not only to the constitution of IPNs but also to the swelling ratio of IPNs. Mechanical property of glutaraldehyde (0.5%) for poly(vinyl alcohol) crosslinking was better than that of glutaraldehyde (1.0%). DSC of the IPN films showed only a single glass transition temperature ( T g ) for each sample, and T g data showed a linear relationship with network composition. Morphology was observed a homogeneous structure, indicating the good compatibility and miscibility between PAA and PVA. Potential application of the IPN films in controlled drug delivery was also examined using crystal violet as a model drug. The release rate of the drug was higher at 37°C than 25°C for all IPNs and also increased slightly with decreasing of poly(acrylic acid) content. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci, 2008