High-expansion-ratio PLLA/PDLA/HNT composite foams with good thermally insulating property and enhanced compression performance via supercritical CO2

It has been a great challenge to prepare high-expansion-ratio polylactide (PLA) foam with eminent thermal insulation and compression performance in packaging field. Herein, a naturally formed nanofiller halloysite nanotube (HNT) and stereocomplex (SC) crystallites were introduced into PLA with a supercritical CO2 foaming method to improve foaming behavior and physical properties. The compressive performance and thermal insulation properties of the obtained poly(L-lactic acid) (PLLA)/poly(D-lactic acid) (PDLA)/HNT composite foams were successfully investigated. At a HNT content of 1 wt%, the PLLA/PDLA/HNT blend foam with an expansion ratio of 36.7 folds showed a thermal conductivity as low as 30.60 mW/(m·K). Meanwhile, the compressive modulus of PLLA/PDLA/HNT foam was 115% higher than that of PLLA/PDLA foam without HNT. Moreover, the crystallinity of PLLA/PDLA/HNT foam was dramatically improved after annealing, thus the results showed that compressive modulus of the annealed foam increased by as high as 72%, while it still maintained good heat insulation with the thermal conductivity of 32.63 mW/(m·K). This work provides a green method for the preparation of biodegradable PLA foams with admirable heat resistance and mechanical performance.