Fatigue crack propagation from a crack inclined to the cyclic tensile axis

Cyclic stresses with stress ratio R = 0.65 were applied to sheet specimens of aluminium which have an initial crack inclined to the tensile axis at angles of 30°, 45°, 72° or 90°. The threshold condition for the non-propagation of the initial crack was found to be given by a quadratic form of the ranges of the stress intensity factors of modes I and II. The direction of fatigue crack extension from the inclined crack was roughly perpendicular to the tensile axis at stress ranges just above the threshold value for non-propagation. On the other hand, at stress ranges 1.6 times higher than the threshold values the crack grew in the direction of the initial crack. The rate of crack growth in the initial crack direction was found to be expressed by the following function of stress intensity factor ranges of mode I, K1, and mode II, K2: dcdN = C(Keff)sum, where Keff = [K14 + 8K24]14. This law was derived on the basis of the fatigue crack propagation model proposed by Weertman.