Effects of Micro-Arc Oxidation Surface Treatment on the Corrosion Resistance of Ti-6Al-4V Electron-Beam-Welded Joints

Micro-arc oxidation (MAO) is performed on Ti-6Al-4V electron-beam-welded joints, and the microstructure, phase composition, and corrosion resistance of the joint and surface coating are investigated systematically by scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDS), X-ray diffraction (XRD), as well as electrochemical and stress corrosion analyses. SEM analyses revealed that the joint undergoes a phase transformation. The coating morphology of the joint and base materials is similar, but the joint coating is denser and thicker. XRD analyses recognize the rutile and anatase phases in the coating. Polarization and electrochemical impedance spectroscopy (EIS) corrosion tests reveal that the MAO treatment results in a decrease of two orders of magnitude in the corrosion current density of the welded joint and an increment of corrosion resistance. Stress corrosion evaluation reveals that a dense layer is exposed to protect the joint after long-term exposure to a high-stress corrosion environment. No stress corrosion-induced cracking or defects are observed in the joints, indicating the corrosion resistance of the joint has significantly improved.