A route toward fabrication of 3D printed bone scaffolds based on poly(vinyl alcohol)–chitosan/bioactive glass by sol–gel chemistry

Among different methods for the fabrication of bone scaffolds, 3D printing has created great advances in tissue engineering and regenerative medicine owing to its ability to make objects mimicking native tissues. Thanks to its abundant availability, structural features, and favorable biological properties, chitosan (CS) hydrogel was selected to be used for preparation of the bone scaffolds. However, the 3D printing of CS-based hydrogels is still under early exploration. Knowing the fact that natural polymers are not so competent at holding large amounts of water, poly(vinyl alcohol) as the second polymer was employed. The novelty of the present research lies in the concept of employing sol-gel chemistry in order to attain proper viscosity and rheological behavior to give self-standing filaments of the polymer blends. Employing sol-gel reaction in the preparation of the hybrid hydrogels had the advantage of endowing shape fidelity to the polymer blend without any solidifying in the needle. The obtained organic-inorganic hybrids were directly printed and subsequently cross-linked. The best performance in terms of mechanical strength, cell viability, and bio-mineralization was observed for the 50:50 ratio. The in vitro cell culture and the bioactivity results showed that the printed scaffolds with this method have great potential in bone tissue engineering. Further, this method could be expandable to print other hydrogels with diverse applications such as implantable devices, soft robotics, etc.