Unusual Fatigue Crack Growth Behavior of Long Cracks at Low Stress Intensity Factor Ranges

In this article, we characterize and review the unusual lack of threshold in fatigue crack growth (FCG) behavior for some alloys at low values of stress intensity factor ranges ΔK and its implications to damage-tolerant design approaches. This unusual behavior was first observed by Marci in 1996 in IMI 834 alloy. Conventional applications of linear elastic fracture mechanics to FCG analysis at constant R-ratio (or K