Effect of Force and Heat Coupling on Machined Surface Integrity and Fatigue Performance of Superalloy GH4169 Specimens

GH4169 is one of the key materials used to manufacture high-temperature load-bearing parts for aero-engines, and the surface integrity of these parts in service conditions significantly affects their high-temperature fatigue performance. Under a coupling effect of high temperature and alternating load, the evolution process of the machined surface integrity index of superalloy GH4169 specimens was studied, and fatigue performance tests at 20 °C, 450 °C, and 650 °C were carried out to analyze the primary factors affecting the high-temperature fatigue performance of specimens. The results indicated that the surface roughness of specimens remained essentially unchanged. However, the value of surface residual stress decreased significantly, with a release of more than 60% at the highest temperature. At 650 °C, the surface microhardness increased, while the degree of surface plastic deformation decreased under alternating loads. Simultaneously, when the surface roughness was less than Ra 0.4 μm, surface microhardness was the main factor affecting the high-temperature fatigue performance of specimens. The influence of surface microhardness on low-cycle fatigue performance was not consistent with that on high-cycle fatigue performance. The latter increased monotonically, whereas the former initially increased and then decreased with increasing surface microhardness.