High-entropy transparent (Y0.2La0.2Gd0.2Yb0.2Dy0.2)2Zr2O7 ceramics as novel phosphor materials with multi-wavelength excitation and emission properties

High-entropy ceramics have been extensively studied because of their novel intrinsic properties and have significant potential for application in various fields. In this study, a novel high-entropy transparent ceramic phosphor (Y0.2La0.2Gd0.2Yb0.2Dy0.2)2Zr2O7 was successfully prepared via a solid-state reaction and vacuum sintering. X-ray diffraction and scanning electron microscopy analyses were performed to analyze the phases and microstructures of the as-prepared powders and sintered ceramics. The highest in-line transmittance of the developed ceramic was 74 % in both visible and infrared regions. To reveal its luminescent properties as a potential WLED material, the photoluminescence of ceramic samples was analyzed using multi-excitation and emission spectra. Strong emissions originating from Dy3+ and Gd3+ were observed, and the emission color was effectively regulated under multi-wavelength excitation. Combining excellent optical transmittance with unique photoluminescence performance, the (Y0.2La0.2Gd0.2Yb0.2Dy0.2)2Zr2O7 high-entropy transparent ceramics can find potential applications as a novel WLED material with multi-wavelength excitation and tunable emission.