Preparation, thermal, and flammability of halogen‐free flame retarding thermoplastic poly(ether‐ester) elastomer/montmorillonite nanocomposites

In this article, the nanocomposites thermoplastic polyester‐ether elastomer (TPEE) with phosphorous–nitrogen (P–N) flame retardants and montmorillonite (MMT) was prepared by melt blending.The fire resistance of nanocomposites was analyzed by limiting oxygen index (LOI) and vertical burning (UL94) test. The result shows that the flame retardants containing P–N increased the LOI of the material from 17.3 to 27%. However, TPEE containing P–N flame retardants just got UL94 V‐2 ranking, which resulted in the flaming dripping phenomenon. On the other hand, TPEE containing P–N flame retardant and organic‐modified montmorillonite (o‐MMT) achieved UL94 V‐0 rating for the special microstructure. The XRD and TEM morphology has demonstrated that the formation of multi‐ordered structure regarding restricted segmental motions at the organic–inorganic interface and stronger interactions between the clay mineral layers and the polymer chains. The structure was supported by the results of rheological properties and DSC analysis. The thermal degradation and char residue characterization was studied by thermal gravimetric analysis (TGA) and SEM‐EDX measurements, respectively. The TGA and SEM‐EDX have demonstrated that o‐MMT results in the increase of char yield and the formation of the thermal stable carbonaceous char. POLYM. COMPOS., 37:700–708, 2016. © 2014 Society of Plastics Engineers