Lithium Recovery from Used Li-Ion Batteries Using Innovative Electrodialysis Method with Lithium Ionic Superconductor

In recent years, the industrial importance of lithium (Li) has increased due to its use in Li-ion batteries. For example, large-sized Li-ion batteries are used as power supplies for electric vehicles and for storage of electricity in smart grids and smart houses. Therefore, a large amount of Li is required worldwide. The extraction of Li from used Li-ion batteries would allow a large amount of Li to be inexpensively acquired. The technology for recycling cobalt (Co) and nickel (Ni) from used Li-ion batteries has already been established. On the contrary, the technology for recycling Li from used Li-ion batteries is not yet established. I have developed a method for the recovery of Li from seawater using a Li ionic superconductor functioning as a Li-ion separation membrane (LISM) [1]. Only Li ions were successfully recovered from seawater through the LISM; other ions in the seawater did not permeate the membrane. Therefore, I have developed an innovative new method for recycling Li from used Li-ion batteries using the LISM. Figure shows the proposed Li recovery method. This innovative method involves the use of an LISM whereby only Li ions in a solution of used Li-ion batteries permeate from the positive electrode side to the negative electrode side during electrodialysis; the other ions, including Co, Al, and F, do not permeate the membrane. Li 0.29 La 0.57 TiO 3 was selected as the LISM because it exhibits high durability against water. The positive side of the dialysis cell was filled with used Li-ion battery solution, supplied by DOWA ECO-SYSTEM Co., Ltd., Japan; the Li concentration of the solution was 2543.5 mg/L. Then the negative side was filled with distilled water. The applied dialysis voltage was 5 V, and electrode area was 16 cm 2 . The calculation of the Li recovery ratios for this first of a kind electrodialysis technique with an LISM sheet was performed. The Li recovery ratio increased with electrodialysis time, reaching approximately 10% at 72 h of dialysis. The recovery ratios of Co, Al, and F were not calculated because the concentrations of Co, Al, and F were below the detection limit of inductively coupled plasma atomic emission spectrometry (ICP-AES). After electrodialysis, CO 2 gas was bubbled in the Li recovery water to produce lithium carbonate (Li 2 CO 3 ) as a raw material for Li-ion batteries. The Li 2 CO 3 deposition was easily generated by the reaction of CO 2 gas and the Li recovery solution as a lithium hydroxide (LiOH) solution. This new method for recycling Li-ion batteries shows good energy efficiency and is easily scalable. Thus, this electrodialysis method is suitable for the recovery of Li from used Li-ion batteries. [1] T. Hoshino, Desalination, 359, 59-63 (2015). Figure 1