Polyoxovanadate Li7[V15O36(CO3)] and its derivative γ-LiV2O5 as superior performance cathode materials for aqueous zinc-ion batteries

Recently, many reports have been published about polyoxovanadates (POVs) with multiple electrons redox activity for energy storage. However, they are easily transformed into solid-state oxides after calcination. We noted that although dehydrated Li7[V15O36(CO3)] (Li7V15) exhibited a high capacity for lithium-ion batteries (LIBs), it was reported that the electrochemical behavior of the dehydrated sample same as γ-LiV2O5 (γ-LVO) which prepared by annealing the cluster and undehydrated Li7V15 was not redox-active. Interestingly, we were surprised to find that undehydrated Li7V15 and its derivative γ-LVO showed better electrochemical performance than LIBs when first proposed as the cathode to store Zn2+. Both Li7V15 and γ-LVO electrodes provided excellent rate performance and satisfied cyclability (135.0 and 214.1 mAh/g at 3 A/g after 1000 cycles, respectively). The fast kinetics of Li7V15 and γ-LVO were verified by pseudocapacitive analysis, GITT and EIS tests. Moreover, the Zn2+ storage mechanism and redox behavior of Li7V15 and γ-LVO were examined by ex-situ measurements. First-principles calculations revealed that the Zn2+ was chemisorbed on the clusters and physisorbed between the clusters. This work enriches the POVs cathode chemistry in aqueous energy storage.