Enhancement of tensile toughness of poly(lactic acid) (PLA) through blending of a polydecalactone-grafted cellulose copolymer: The effect of mesophase transition on mechanical properties

Increasing the toughness of poly(lactic acid) (PLA), i.e., simultaneously increasing both the tensile strength and ductility, remains a major challenge. In this study, fully bio-based PLA blends with polydecalactone (PDL)-grafted cellulose copolymer (CgPD) were prepared and comprehensively analyzed to enhance the toughness of the PLA matrix. The blends were found by FT-IR and solid-state 1H NMR to be physically intact and miscible at the sub-twenty-nanometer scale. The WXRD and DSC analyses indicated that the addition of the alkyl-branched CgPD imparts a more structurally disordered PLA mesophase state to the prepared PLA_CgPD bio-blends. UTM analysis was used to characterize the macroscopic mechanical properties of the PLA_CgPD bio-blends. Both the tensile strength and elongation properties were simultaneously improved with the addition of 1 wt% CgPD loading amount to PLA (PLA_CgPD1). This study experimentally demonstrates that the enhanced mechanical properties of PLA_CgPD1 are closely related to the existence of more ordered PLA mesophases induced by the introduction of an optimal amount of CgPD into the PLA matrix.