Some effects of polymer addition on the fire resistance of concrete

Some trials have been made under this work to see the influence of small amount (1–1.5%) polymer addition on the fire resistance of concrete. Normal concrete plates with and without polymer addition are compared. Lightweight aggregate concrete plates, slabs and reinforced beams are also tested for fire exposure. Plates of normal and lightweight aggregate concrete have not shown any spalling effect when exposed to fire from one side. Normal concrete without polymer addition resulted in explosive spalling when exposed to fire from two sides whereas no spalling is noticed in all types of concrete tested with polymer addition. A more open structure created in cement paste by polymer addition seems to facilitate the steam transport from the specimens during heating and thus prevents creation of high vapor pressure in the concrete, responsible for explosive spalling. I detta arbete har några försök genomförts i syfte att studera små polymertillsatsers (1–1,5%) inverkan på betongens brandbeständighet. En jämförande studie har gjorts mellan oarmerade konventionella betongplattor med och utan polymertillsats. Dessutom har brandbeständighetsförsök genomförts på plattor av armerad lättballastbetong. Plattorna av konventionell betong och lättballastbetong uppvisade inga avflagningsskador vid ensidig brandbelastning. Då plattorna utsattes för dubbelsidig brandbelastning uppstod explosiva avflagningsskador på plattorna av konventionell betong utan polymertillsats. För de övriga plattorna med polymertillsats erhölls inga avflagningsskador. En mer öppen struktur i cementpastan, orsakad av polymertillsatsen, tycks underlätta vattenångtransporten ut ur provkropparna under uppvärmningsskedet och förhindra uppkomsten av högt ångtryck i betongen, vilket förorsakar explosiv avflagning.