Exploring the Influence of Nanocrystalline Structure and Aluminum Content on High-Temperature Oxidation Behavior of Fe-Cr-Al Alloys

The present study examines the high-temperature (500–800 °C) oxidation behavior of Fe-10Cr-(3,5) Al alloys and studies the effect of nanocrystalline structure and Al content on their resistance to oxidation. The nanocrystalline (NC) alloy powder was synthesized via planetary ball milling. The prepared NC alloy powder was consolidated using spark plasma sintering to form NC alloys. Subsequently, an annealing of the NC alloys was performed to transform them into microcrystalline (MC) alloys. It was observed that the NC alloys exhibit superior resistance to oxidation compared to their MC counterparts at high temperatures. The superior resistance to oxidation of the NC alloys is attributed to their considerably finer grain size, which enhances the diffusion of those elements to the metal–oxide interface that forms the protective oxide layer. Conversely, the coarser grain size in MC alloys limits the diffusion of the oxide-forming components. Furthermore, the Fe-10Cr-5Al alloy showed greater resistance to oxidation than the Fe-10Cr-3Al alloy.