Fire-safe epoxy composite realized by MXenes based nanostructure with vertically arrayed MOFs derived from interfacial assembly strategy

In this contribution, Ni-based metal organic frameworks (Ni-MOF) nanosheets with high specific surface area are grown on transition metals carbides (MXenes, denoted as MX) surface via vertical alignment, gestating the flame retardant of [email protected] With the addition of 2.0 wt% [email protected], the peak heat release rate, peak smoke production rate, peak CO production rate, peak CO2 production rate are reduced by 42.5 %, 26.7 %, 37.8 %, 54.9 %, while the peak concentrations of C2H6, CH4, HCN, NO, N2O are impaired by 91.3 %, 94.3 %, 89.6 %, 90.3 %, 60.9 %, suggesting the enhanced fire safety. Meantime, the fire performance index is elevated by 83.0 % and fire growth index is reduced by 37.2 %, demonstrating the promoted fire safety. Of note, the using of [email protected] induces the promotion of 787.1 % in char yield after combustion, which shows higher graphitized degree and thus enables better protection for basal matrix. Flame retardation contrast with previous works also manifests the strength of [email protected] in hindering the heat release and toxicants emission. This work offers a new paradigm for forging fire-safe polymer composites with low toxicity.