Dielectric and piezoelectric properties of porous lead-free 0.5Ba(Ca0.8Zr0.2)O3-0.5(Ba0.7Ca 0.3)TiO3 ceramics

Porous barium calcium zirconate titanate 0.5Ba(Ca 0.8 Zr 0.2 )O 3 -0.5(Ba 0.7 Ca 0.3 )TiO 3 (BCZT) lead-free ferroelectric ceramics were fabricated via a burnt polymer spheres (BURPS) technique by introducing corn starch as the pore-forming agent. The effect of porosity on the microstructure, dielectric, and piezoelectric properties of the porous materials were investigated. An increase in porosity volume fraction from 10% to 25% resulted in an increase in the hydrostatic charge coefficient ( d h ), which was 140 to 560% higher than that of the dense BCZT material. An increase in porosity fraction from 10% to 25% also lead to a decrease in relative permittivity that was 16.7% to 60.4% lower than the dense material. These two changes in properties provided a significant enhancement of the hydrostatic figure of merit ( d h ∙ g h ) for the porous ceramic; for example the d h ∙ g h of the 25 vol.% porous BCZT ceramic was 158 times more than the dense ceramic and demonstrates the potential of porous lead-free ferroelectrics for piezoelectric transducer devices. Reasons for the significant enhancement in piezoelectric performance of the porous ceramics are discussed.