A novel method for fabricating brick-mortar structured alumina-zirconia ceramics with high toughness

The present work reports a novel and simple approach to prepare alumina-zirconia composites with superior toughness. Alumina microspheres were innovatively used as the raw materials, followed by coating zirconia and hot-pressing sintering to fabricate alumina-zirconia ceramics. The resultant ceramics are given a unique brick-mortar microstructure, in which the zirconia “mortar” layers continuously distribute around the alumina “brick” matrix, leading to outstanding fracture toughness of 7.34 MPa·m1/2 and high strength of 635.84 MPa when prepared with zirconia contents of 10 wt%. The major explanation could be ascribed to that crack tips in sintered samples tend to propagate along the zirconia “mortar” layer, accompanied by deflection and branching, which effectively improve the fracture toughness of composites. The uniformity and integrity of the brick-mortar structure could be well tuned by varying the amount of zirconia. This method has reference significance for the preparation of high toughness alumina-based multiphase ceramics.